ASTM B117-07A PDF

The salt spray (or salt fog) test is a standardized and popular corrosion test method, used to ASTM B was the first internationally recognized salt spray standard, originally published in Other important relevant standards are. Designation: B – 07a Standard Practice for Operating Salt Spray (Fog) Apparatus1 This standard is issued under the?xed designation B. ASTM B Testing, also known as a Standard Practice for Operating Salt ASTM B Testing requires controls over many operational parameters such as: .

Author: Nekree Balmaran
Country: Brazil
Language: English (Spanish)
Genre: Travel
Published (Last): 24 July 2004
Pages: 193
PDF File Size: 2.28 Mb
ePub File Size: 3.55 Mb
ISBN: 584-9-77368-465-9
Downloads: 56043
Price: Free* [*Free Regsitration Required]
Uploader: Fausho

Once a year the corrosivity of the salt spray test chamber has to be checked.

SaliCORR® ASTM B Sodium Chloride

The distribution of the salt fog inside the test chamber has to be regularly checked. This may be accomplished by placing the apparatus zstm a constant-temperature room, but may also be achieved by surrounding the basic chamber of a jacket containing water or air at a controlled temperature.

Room air may be compressed, heated, humidi? This test can be used to test the relative resistance to corrosion of aluminium alloys when exposed to a changing climate of acetic acid salt spray, followed by air drying, followed by high humidity, all at an elevated temperature.

ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentioned in this standard.

Exhaust at opposite side of test space from spray nozzle Item 12but preferably in combination with drain, waste trap, and forced draft waste pipe Items 16, 17, and Test specimens are placed in an enclosed chamber and exposed to a continuous indirect spray of salt water solution, prepared in accordance with the requirements of the test standard and acidified to pH 3. Salt spray testing is an accelerated corrosion test that produces a corrosive attack to coated samples in order to evaluate mostly comparatively the suitability of the coating for use as a protective finish.

Otherwise, the test specimens shall consist of steel meeting the requirements of Practice D and shall be cleaned and prepared for coating in accordance with the applicable procedure of Practice D Is VLM only a distributor of corrosion test chambers? Test solution tank L complete with tankfilter,hose and fitting. Although there may be a weak correlation between the duration in salt spray test and the expected life of a coating in certain coatings such as hot dip galvanized steelthis test has gained worldwide popularity due to low cost and quick results.

  FABULAS PANICAS ALEJANDRO JODOROWSKY PDF

Suitable apparatus which may be used is described in Appendix X1. Please log in, in order to get access to prices, ordering and inquiry functions. Most commonly, the time taken for oxides to appear on the samples under test is compared to expectations, to determine whether the test is passed or failed.

All other water will be referred to as reagent grade. A common method of introducing the air is through an air dispersion device X1. Test, Measure and Control. This is followed by 1. Nozzles are not necessarily located at one end, but may be placed in the center and can also be directed vertically up through a suitable tower. This formula yields a result of 53 g 1.

A solution that requires between 3. Heating Blocks for Evaporators.

Salt spray test

Slotted wooden strips are suitable for the support of? Cyclic corrosion testing is better suited to b117-07q. Suitably located and directed spray nozzles avoid ceiling accumulation and drip.

In either case, the exposure to salt spray may be salt water spray or synthetic sea water prepared in accordance with the requirements of the test standard. Salt spray testing is popular because it is relatively inexpensive, quick, well standardized, and reasonably repeatable.

Operations shall be so scheduled that these interruptions are held to a minimum. ISO standards by standard number. Results are represented generally as testing hours in NSS without appearance of corrosion products e. ASTM G85 is an example of a test standard which contains several modified salt spray tests satm are variations to the basic salt spray test. However, in order to obtain reliable results additional requirements must be met. The second climate cycle comprises 0.

There is a general historical consensus that larger chambers can provide a more homogeneous testing environment. It is preferred that control panels be provided that bracket the expected test specimen performance. Preparation of Test Specimens 6. Most Salt Spray Chambers today are being used NOT to predict the corrosion resistance of a coating, but to maintain coating processes such as pre-treatment and painting, electroplating, galvanizing, and the like, on a comparative basis.

  EL CAMINO ABIERTO POR JESUS PAGOLA PDF

When the pH of the salt solution is adjusted to 6.

SAL 3000-FL

Sstm from glass hooks or waxed string may be used as long as the speci? NOTE 7—If the tower is run outside of these suggested temperature and pressure ranges to acheive proper collection rates as described in This does not apply to running tap water.

This design principle provides, in contrary to the test chambers made of glass reinforced plastic, much better thermal conductivity which is aatm prerequisite for the reproducibility of the test atmospheres in modern corrosion test procedures. Funnels and dishes with a diameter of 10 cm 3.

Specimens shall preferably be supported from the bottom or the side. This acceleration arises through the use of chemically altered salt spray solutions, often combined with other test climates and in most cases, the relatively rapid cycling of these test climates over time.

However, these testing standards neither provide information of testing periods for the coatings to be ast, nor the appearance of corrosion products in form of salts. NOTE 1—Should b117-07s be desirable to cut test specimens from parts or from preplated, painted, or otherwise coated steel sheet, the cut edges shall be protected by coating them with paint, wax, tape, or other effective media so that the development of a galvanic effect between such edges and the adjacent plated or otherwise coated metal surfaces, is prevented.

The cleaning method shall be optional depending on the nature of the surface and the contaminants. It is preferable to saturate the air at temperatures well above the chamber temperature as insurance of a wet fog as listed in Table 2. Unit for filtering compressed air. NOTE 2—Suitable materials for the construction or coating of racks and supports are glass, rubber, plastic, or suitably coated wood.

The salt spray test is one of the most widespread and long established corrosion tests.